Contents 1 Application 2 Appearance and use 3 Early history 4 Later developments 5 See also 6 References 7 Sources 8 External links


Application[edit] The process involves submerging the metal part into a phosphoric acid solution whose key ingredient is often zinc or manganese, with varying additional amounts of nitrates, chlorates, and copper. In one of the many processes that have been developed, the solution is heated to a temperature of 88–99 °C (190–210 °F) for a period ranging between 5 and 45 minutes. A stream of small bubbles is emitted from the metal part as the process takes place; when the bubbling stops, the process is complete. In addition to this particular processing temperature, there have also been various similar Parkerizing processes developed and patented that permit using either lower temperatures (for energy efficiency) or higher temperatures (for faster processing). The Parkerizing reaction equation in a metal-phosphate-solution is as follows: 2 Fe(s) + Fe3+ (aq) + 3 H2PO4− (aq) → 3 FePO4(s) + 3 H2 (g)


Appearance and use[edit] Zinc phosphating results in a non-reflective, light- to medium-gray finish. Manganese phosphating produces a medium- to dark-gray or black finish. Iron phosphating produces a black or dark gray finish similar to manganese phosphating. The grain size of the zinc phosphating is usually the smallest among the three processes, providing a more appealing cosmetic appearance in many applications. Some parkerized guns, particularly of WWII vintage, have almost OD green color. This was caused by contaminants in the acid solution and not cosmoline as is commonly believed. Manganese and iron phosphating coatings are usually the thickest electrochemical conversion coatings, being thicker than electrochemical conversion coatings such as zinc phosphating and bluing. As for other chemical conversion coatings, the Parkerized surface must be completely covered with a light coating of oil to maximize corrosion and wear resistance, primarily through reducing wetting action and galvanic action. A heavy oil coating is unnecessary and undesirable for achieving a positive grip on Parkerized metal parts. Alternatively, the Parkerized surface may be painted over with an epoxy or molybdenum finish for added wear resistance and self-lubricating properties.


Early history[edit] Development of the process was started in England and continued by the Parker family in the United States. The terms Parkerizing, Parkerize, and Parkerized are all technically registered U.S. trademarks of Henkel Adhesives Technologies, although the terminology has largely passed into generic use for many years. The process was first used on a large scale in the manufacture of firearms for the United States military during World War II.[1] The earliest work on phosphating processes was developed by British inventors William Alexander Ross, British patent 3119, in 1869, and by Thomas Watts Coslett, British patent 8667, in 1906. Coslett, of Birmingham, England, subsequently filed a patent based on this same process in America in 1907, which was granted U.S. Patent 870,937 in 1907. It essentially provided an iron phosphating process, using phosphoric acid. An improved patent application for manganese phosphating based in large part on this early British iron phosphating process was filed in the US in 1912, and issued in 1913 to Frank Rupert Granville Richards as U.S. Patent 1,069,903. Clark W. Parker acquired the rights to Coslett's and Richards' U.S. patents, and experimented in the family kitchen with these and other rust-resisting formulations. The ultimate result was that Clark W. Parker, along with his son Wyman C. Parker, working together, set up the Parker Rust-Proof Phosphating Company of America in 1915. Colquhoun of the Parker Rust-Proof Phosphating Company of America then filed another improved phosphating patent application in 1919. This patent was issued in 1919 as U.S. Patent 1,311,319, for an improved manganese phosphating (Parkerizing) technique. Similarly, Baker and Dingman of the Parker Rust-Proof Company filed an improved manganese phosphating (Parkerizing) process patent in 1928 that reduced the processing time to ​1⁄3 of the original time that had been required through heating the solution to a temperature in the precisely controlled range of 500 to 550 °F (260 to 288 °C). This patent was issued as U.S. Patent 1,761,186 in 1930. Manganese phosphating, even with these process improvements, still required the use of expensive and difficult-to-obtain manganese compounds. Subsequently, an alternative technique was developed by the Parker Company to use easier-to-obtain compounds at less expense through using zinc phosphating in place of manganese phosphating. The patent for this zinc phosphating process (using strategic compounds that would remain available in America during a war) was granted to inventor Romig of the American Chemical Paint Company in 1938 as U.S. Patent 2,132,883, just prior to the loss of easy access to manganese compounds that occurred during World War II. Somewhat analogous to the improved manganese phosphating process improvements discovered by Baker and Dingman, a similarly improved method was found for an improved zinc phosphating process as well. This improvement was discovered by Darsey of the Parker Rust Proof Company, who filed a patent in February 1941, which was granted in August 1942, U.S. Patent 2,293,716, that improved upon the zinc phosphatizing (Parkerizing) process further. He discovered that adding copper reduced the alkalinity requirement over what had been required, and that also adding a chlorate to the nitrates that were already used would additionally permit running the process at a much lower temperature in the range of 115 to 130 °F (46 to 54 °C), reducing the cost of running the process further. With these process improvements, the end result was that a low-temperature (energy-efficient) zinc phosphating (Parkerizing) process, using strategic materials to which the United States had ready access, became the most common phosphating process used during World War II to protect American war materials such as firearms and planes from rust and corrosion.


Later developments[edit] Glock 17 pistol with a black Parkerized topcoat. Glock Ges.m.b.H., an Austrian firearms manufacturer, uses a black Parkerizing process as a topcoat to a Tenifer process to protect the slides of the pistols they manufacture. After applying the Tenifer process, a black Parkerized finish is applied and the slide is protected even if the Parkerized finish were to wear off. Used this way, Parkerizing is thus becoming a protective and decorative finishing technique that is used over other underlying improved techniques of metal protection. Traditional iron phosphate, zinc phosphate, and manganese phosphate chemical conversion coatings, including Parkerizing variations, have all been criticized[2] in recent years for introducing phosphates into surface water systems, encouraging the rapid growth of algae (eutrophication). As a result, in recent years, new, emerging technology alternatives to traditional phosphate coatings have started to see limited use, for replacing all phosphating coatings, including Parkerizing. The majority of these newer conversion coatings are fluorozirconium-based. The most popular of these fluorozirconium-based conversion coatings, introduced in 2005, incorporates the transition metal vanadium. This new, more environmentally friendly coating is referred to as a vanadate conversion coating. Besides vanadate coatings, arsenate coatings may theoretically provide similar protection, at the risk of being a health hazard to humans and animals. It remains to be seen if these, or other new chemical conversion coatings, will ultimately replace traditional phosphating and Parkerizing. Various if similar recipes for stovetop kitchen Parkerizing circulate in gun publications at times, and Parkerizing kits are sold by major gun-parts distributors such as Brownells.


See also[edit] Bluing Ferritic nitrocarburizing Passivation Phosphate minerals


References[edit] ^ "Just The Facts". Calvan.com. Retrieved April 12, 2014.  ^ U.S. Environmental Protection Agency Recommendations


Sources[edit] MIL-HDBK-205, Phosphate & Black Oxide Coating of Ferrous Metals: a standard overview on phosphate and black oxide (bluing) coatings Budinski, Kenneth G. (1988), Surface Engineering for Wear Resistance, Englewood Cliffs, New Jersey: Prentice Hall, p. 48  Brimi, Marjorie A. (1965), Electrofinishing, New York, New York: American Elsevier Publishing Company, Inc., pp. 62–63 .


External links[edit] Henkel Surface Technologies—Current owner of Parco-Lubrite (a manganese phosphating process) and other Parkerizing rust-prevention coatings. (Parco is a registered trademark of Henkel Surface Technologies.) Coral Chemical Company—Current owner of Coral Eco Treat (vanadium conversion coating process) Parker Rust-Proof of Cleveland—Last remaining of the four original job shop licensees of Parker Chemical, currently offers phosphating services Retrieved from "https://en.wikipedia.org/w/index.php?title=Parkerizing&oldid=825668722" Categories: CoatingsCorrosion preventionMetalworking


Navigation menu Personal tools Not logged inTalkContributionsCreate accountLog in Namespaces ArticleTalk Variants Views ReadEditView history More Search Navigation Main pageContentsFeatured contentCurrent eventsRandom articleDonate to WikipediaWikipedia store Interaction HelpAbout WikipediaCommunity portalRecent changesContact page Tools What links hereRelated changesUpload fileSpecial pagesPermanent linkPage informationWikidata itemCite this page Print/export Create a bookDownload as PDFPrintable version Languages FrançaisРусский Edit links This page was last edited on 14 February 2018, at 18:19. Text is available under the Creative Commons Attribution-ShareAlike License; additional terms may apply. By using this site, you agree to the Terms of Use and Privacy Policy. Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc., a non-profit organization. Privacy policy About Wikipedia Disclaimers Contact Wikipedia Developers Cookie statement Mobile view (window.RLQ=window.RLQ||[]).push(function(){mw.config.set({"wgPageParseReport":{"limitreport":{"cputime":"0.132","walltime":"0.165","ppvisitednodes":{"value":471,"limit":1000000},"ppgeneratednodes":{"value":0,"limit":1500000},"postexpandincludesize":{"value":8136,"limit":2097152},"templateargumentsize":{"value":201,"limit":2097152},"expansiondepth":{"value":7,"limit":40},"expensivefunctioncount":{"value":0,"limit":500},"entityaccesscount":{"value":0,"limit":400},"timingprofile":["100.00% 138.034 1 -total"," 34.66% 47.838 1 Template:Reflist"," 28.24% 38.980 1 Template:Cite_web"," 25.77% 35.574 3 Template:Convert"," 18.15% 25.059 1 Template:About"," 9.62% 13.284 2 Template:Citation"," 3.95% 5.449 2 Template:Su"," 3.13% 4.325 1 Template:Frac"," 2.41% 3.331 6 Template:US_patent"," 1.90% 2.628 1 Template:Zwsp"]},"scribunto":{"limitreport-timeusage":{"value":"0.063","limit":"10.000"},"limitreport-memusage":{"value":3219852,"limit":52428800}},"cachereport":{"origin":"mw1324","timestamp":"20180219030208","ttl":1900800,"transientcontent":false}}});});(window.RLQ=window.RLQ||[]).push(function(){mw.config.set({"wgBackendResponseTime":139,"wgHostname":"mw1263"});});


Parkerizing - Photos and All Basic Informations

Parkerizing More Links

Phosphate Conversion CoatingRobert M. Parker, Jr.Enlarge.45 ACPSteelCorrosionPhosphate Conversion CoatingFirearmBluing (steel)Conversion CoatingAluminiumBrassCopperSteelNickelStainless SteelPassivation (chemistry)Phosphoric AcidZincManganeseNitrateChlorateCopperIronHydrogenPhosphorusOxygenIron(III) PhosphateOlive (color)CosmolineOilWearGalvanic CorrosionEpoxyMolybdenumLubricatingUnited StatesTrademarkGenericized TrademarkWorld War IIBirmingham, EnglandPhosphoric AcidStrategic MaterialWorld War IIEnlargeGlockGlock Ges.m.b.H.AustriaTeniferPistol SlidePistolsEutrophicationVanadiumVanadateArsenateBluing (steel)Ferritic NitrocarburizingPassivation (chemistry)Phosphate MineralsEnglewood Cliffs, New JerseyNew York, New YorkHelp:CategoryCategory:CoatingsCategory:Corrosion PreventionCategory:MetalworkingDiscussion About Edits From This IP Address [n]A List Of Edits Made From This IP Address [y]View The Content Page [c]Discussion About The Content Page [t]Edit This Page [e]Visit The Main Page [z]Guides To Browsing WikipediaFeatured Content – The Best Of WikipediaFind Background Information On Current EventsLoad A Random Article [x]Guidance On How To Use And Edit WikipediaFind Out About WikipediaAbout The Project, What You Can Do, Where To Find ThingsA List Of Recent Changes In The Wiki [r]List Of All English Wikipedia Pages Containing Links To This Page [j]Recent Changes In Pages Linked From This Page [k]Upload Files [u]A List Of All Special Pages [q]Wikipedia:AboutWikipedia:General Disclaimer



view link view link view link view link view link